- Volume 55
- Issue 2
- Apr 2011
- Pages 74-83
Microstructure Analysis of Selected Platinum Alloys
- By Paolo Battaini
- 8853 SpA, Via Pitagora 11, I-20016 Pero,
- Milano, Italy E-mail: firstname.lastname@example.org
- Platinum Metals Rev.,
Metallographic analysis can be used to determine the microstructure of platinum alloys in order to set up working cycles and to perform failure analyses. A range of platinum alloys used in jewellery and industrial applications was studied, including several commonly used jewellery alloys. Electrochemical etching was used to prepare samples for analysis using optical metallography and additional data could be obtained by scanning electron microscopy and energy dispersive spectroscopy. The crystallisation behaviour of as-cast alloy samples and the changes in microstructure after work hardening and annealing are described for the selected alloys.
Optical metallography is a widely used investigation technique in materials science. It can be used to describe the microstructure of a metal alloy both qualitatively and quantitatively. Here, the term ‘microstructure’ refers to the internal structure of the alloy as a result of its composing atomic elements and their three-dimensional arrangement over distances ranging from 1 micron to 1 millimetre.
Many alloy properties depend on the microstructure, including mechanical strength, hardness, corrosion resistance and mechanical workability. Metallography is therefore a fundamental tool to support research and failure analysis (1–3). This is true for all industrial fields where alloys are used. A great deal of literature is available on the typical methods used in optical metallography (4–6).
A large amount of useful information is available in the literature for precious metals in general (7–10). However, there is less information specifically focussed on platinum and its alloys.
The present work aims to give some examples of platinum alloy microstructures, both in the as-cast and work hardened and annealed conditions, and to demonstrate the usefulness of optical metallography in describing them. This paper is a revised and updated account of work that was presented at the 24th Santa Fe Symposium® on Jewelry Manufacturing Technology in 2010 (11).
Materials and Methods
A wide variety of platinum alloys are used in jewellery (12–18) and industrial applications (10, 19–21). Different jewellery alloys are used in different markets around the world, depending on the specific country's standards for precious metal hallmarking. The alloys whose microstructures are discussed here are listed in
Table I. These do not represent all the alloys available on the market, but were chosen as a representative sample of the type of results that can be obtained using metallographic techniques. The related Vickers microhardness of each alloy sample, measured on the metallographic specimen with a load of 200 gf (∼2 N) in most cases, is given for each microstructure.
The microhardness value refers to the microstructure of samples measured in this study and reported in the captions of the Figures
These alloys are among the most common for jewellery applications. Where it is not specified, it is assumed that the balance of the alloy is platinum
If metallographic analysis is aimed at comparing the microstructure of different alloys in their as-cast condition, the initial samples must have the same size and shape. Mould casting or investment casting can produce different microstructures, with different grain sizes and shapes, depending on parameters such as mould shape, size and temperature, the chemical composition of the mould, etc. Therefore, whenever possible, the specimens for the present study were prepared under conditions which were as similar as possible, including the casting process. The specimens were prepared by arc melting and pressure casting under an argon atmosphere to the shape shown in Figure 1. A Yasui & Co. Platinum Investment was used, with a final flask preheating temperature of 650°C. The captions of the micrographs specify whether the original specimen is of the type described above.
The preparation of the metallographic specimens consists of the following four steps: sectioning, embedding the sample in resin, polishing the metallographic section, and sample etching for microstructure detection. The detailed description of these steps will not be given here, as they have been discussed in other works (4–10).
Further advice relevant to platinum alloys was given in the 2010 Santa Fe Symposium paper (11) and in this Journal (22). In these papers, procedures for the metallographic analysis of most platinum alloys are described. The samples for the present study were prepared by electrolytic etching in a saturated solution of sodium chloride in concentrated hydrochloric acid (37%) using an AC power supply, as described previously (22).
Microstructures of the Platinum Alloys
In this section the microstructures of the selected platinum alloys in different metallurgical conditions are presented. As already stated, this selection is a representative sample and not a complete set of the platinum alloys which are currently on the market.
As-Cast Microstructures: Metallography of Crystallisation
Examination of the as-cast microstructures shows the variation in size and shape of the grains in different platinum alloys. However, a noticeable dendritic grain structure is quite common. The largest grain size was found in platinum with 5 wt% copper (Pt-5Cu) (Figure 2) and platinum with 5 wt% gold (Pt-5Au) (Figure 3), with sizes up to 1 mm and 2 mm, respectively. The Pt-5Au alloy sample also shows shrinkage porosity between the dendrites. The core of the dendritic grains showed a higher concentration of the element whose melting temperature was the highest in both cases. This behaviour, known as ‘microsegregation’, has been widely described (12, 23, 24). Electrolytic etching tended to preferentially dissolve the interdendritic copper- or gold-rich regions, respectively. In a platinum with 5 wt% iridium (Pt-5Ir) alloy (Figure 4), since iridium has the higher melting temperature, the dendritic crystals were enriched in iridium in the first solidification stage.
It is important to point out that the higher or lower visibility of microsegregation within the dendrites is not directly related to the chemical inhomogeneity, but to the effectiveness of the electrolytic etching in revealing it. For example, the microsegregation in the platinum with 5 wt% cobalt (Pt-5Co) alloy is hardly visible in Figure 5, despite being easily measurable by other techniques (24).
Scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) are very effective in showing the presence of microsegregation. Figure 6 shows an as-cast sample of a platinum with 25 wt% iridium and 15 wt% rhodium alloy (60Pt-25Ir-15Rh). The SEM backscattered electron image is shown in Figure 7. The EDS maps in Figures 8–10 give the elemental distribution on the etched surface. If the maps were obtained on the polished surface the approximate concentration of each element may be different due to the etching process and a possible preferential dissolution of different phases of the alloy.
However, because EDS is a semi-quantitative method, it can only give the general distribution of the elements on the metallographic section. It is worthwhile remembering that metallographic preparation reveals only a few microstructural features. By changing the preparation or the observation technique, some microstructural details may appear or become more clearly defined, while others remain invisible.
The melting range of the alloy and the flask preheating temperature affect the size and shape of grains significantly. In order to decrease the dendritic size and obtain a more homogeneous microstructure, the temperature of the material containing the solidifying alloy is lowered as much as possible. The effectiveness of such an operation is, however, limited by the melting range and by the chemical composition of the alloy. An example of the flask temperature effect is shown in Figure 11 for Pt-5Ir poured into a flask with a final preheating temperature of 890°C. This microstructure is to be compared with that in Figure 4, in which a flask preheating temperature of 650°C was used.
A smaller grain size was observed in the platinum with 5 wt% ruthenium (Pt-5Ru) alloy, which showed a more equiaxed grain (Figure 12) with a grain size of about 200 μm. The addition of ruthenium led to finer grains in the platinum alloy.
Pouring the alloy in a copper mould produces a smaller grain size due to the high cooling rate, as visible in Figure 6 and Figures 13–15. In this case, the high iridium and rhodium content also contributed to the lower grain size in the as-cast sample.
Homogenising thermal treatments result in a microstructural change. Comparing Figure 16 with Figure 17 highlights a reduction in microsegregation in Pt-5Cu as a consequence of a homogenisation treatment performed at 1000°C for 21 hours.
Work Hardened and Annealed Microstructures: Metallography of Deformation and Recrystallisation
Optical metallography can reveal the changes in microstructure that occur after work hardening and recrystallisation thermal treatments and allows recrystallisation diagrams like the one in Figure 18 to be drawn. This makes it a valuable aid in setting up working cycles. It is necessary to establish the right combination of plastic deformation and annealing treatment in order to restore the material's workability. This allows suitable final properties to be achieved.
An example of the changes in microstructure after various stages of work hardening and annealing is shown in Figure 19 for the 60Pt-25Ir-15Rh alloy. This can be compared to the as-cast structure shown in Figure 6.
Drawn wires show a very different microstructure along the drawing (longitudinal) direction in comparison to the transverse direction (Figures 20–22 for Pt-5Au). However, after annealing, the microstructure becomes homogeneous and the fibres formed after to the drawing procedure are replaced by a recrystallised microstructure (Figures 23 and 24). Using the techniques described elsewhere (11), analyses can be performed even on very thin wires, as shown in Figure 25 for a platinum 99.99% wire of 0.35 mm diameter.
It is worth pointing out that some binary platinum alloys have a miscibility gap at low temperatures, as shown by their phase diagrams (19, 20, 25). Examples of this are given in Figures 26 and 27 for Pt-Ir and Pt-Au, respectively. Similar behaviour is observed for Pt-Co, Pt-Cu and Pt-Rh alloys.
As a consequence, a biphasic structure is expected of each of them. However, this may not occur for various reasons. The phase diagrams refer to equilibrium conditions, which hardly ever correspond to the as-cast conditions. One of the two phases is sometimes present but in low volumetric fraction, due to the chemical composition of the alloy, in which one of the two elements has a low concentration. Furthermore, the thermal treatments may have homogenised the alloy. Finally, the metallographic preparation may not be able to reveal such biphasic structures. Therefore, it is necessary to use other analytical techniques to detect the type and concentration of the alloy phases. Only in specific cases can the biphasic structure be revealed.
The best results in working platinum alloys are generally achieved by hot forging the ingot during the first stages of the procedure. Metallography shows the differences between a material that has been cold worked and annealed (Figures 28 and 29 for Pt-5Cu) and a material that has been hot forged (Figures 30 and 31). Hot forging more easily achieves a homogeneous and grain-refined microstructure, free of defects. This is due to the dynamic recrystallisation that occurs during hot forging (26).
The Limits of Metallography
Optical metallography is only the first step towards the study of the microstructure of an alloy. A wide variety of analytical techniques can be used alongside it to provide a far more complete knowledge of the microstructure. One of the most widely used techniques is SEM. In addition to this, EDS allows the relative concentration of the contained chemical elements to be determined, as shown in Figures 8–10. Further studies can be performed by X-ray diffraction (XRD), which reveals the different crystal phases present in the alloy.
When working with platinum alloys, often only very small specimens are available, therefore more recent techniques may be required in order to study them. One of these is the focused ion beam (FIB) technique, which can produce microsections of a specimen (27, 28). The microsections are then analysed by other techniques, such as transmission electron microscopy (TEM). In this case the details of microstructure can be detected due to the high spatial resolution of the technique. The crystal structure of the primary and secondary phases can be studied by electron diffraction. Another interesting technique is nano-indentation, performed with micron-sized indenters, which allows hardness measurements to be performed with a spatial resolution far better than that attainable with ordinary micro-indenters. The data obtained from these measurements allows the measurement of fundamental mechanical properties of the alloy, such as the elastic modulus (Young's modulus) (29).
The metallographic analysis of platinum alloys can be profitably carried out by using a specimen preparation methodology based on the techniques used for gold-based alloys. However, electrochemical etching is required in order to reveal the alloy microstructure and observe it by optical microscopy. A saturated solution of sodium chloride in concentrated hydrochloric acid can be successfully used for a great many platinum alloys, both in the as-cast condition and after work hardening. Optical metallography provides essential data on the alloy microstructure which can be used in setting up the working procedures. Other techniques can be used alongside it to achieve a more complete knowledge of the material, the effects of the working cycles on it, and to interpret and explain any remaining problems.
- S. Grice, ‘Know Your Defects: The Benefits of Understanding Jewelry Manufacturing Problems’, in “The Santa Fe Symposium on Jewelry Manufacturing Technology 2007”, ed.E. Bell, Proceedings of the 21st Symposium in Albuquerque, New Mexico, USA, 20th–23rd May, 2007, Met-Chem Research Inc, Albuquerque, New Mexico, USA, 2007, pp. 173–211
- P. Battaini, ‘Metallography in Jewelry Fabrication: How to Avoid Problems and Improve Quality’, in “The Santa Fe Symposium on Jewelry Manufacturing Technology 2007”, ed.E. Bell, Proceedings of the 21st Symposium in Albuquerque, New Mexico, USA, 20th–23rd May, 2007, Met-Chem Research Inc, Albuquerque, New Mexico, USA, 2007, pp. 31–65
- “Failure Analysis and Prevention”, eds.R. J. Shipley and W. T. Becker, ASM Handbook, Volume 11, ASM International, Ohio, USA, 2002
- G. F. Vander Voort, “Metallography: Principles and Practice”, Material Science and Engineering Series, ASM International, Ohio, USA, 1999
- “Metallography and Microstructures”, ed.G. F. Vander Voort, ASM Handbook, Volume 9, ASM International, Materials Park, Ohio, USA, 2004
- G. Petzow, “Metallographic Etching”, 2nd Edn., ASM International, Ohio, USA, 1999
- T. Piotrowski and D. J. Accinno, Metallography, 1977, 10, (3), 243 LINK http://dx.doi.org/10.1016/0026-0800(77)90031-3
- D. Ott and U. Schindler, Gold Technol., 2001, 33, 6
- “Standard Practice for Microetching Metals and Alloys”, ASTM Standard E407, ASTM International, West Conshohocken, Pennsylvania, USA, 2007 LINK http://dx.doi.org/10.1520/E0407-07
- E. M. Savitsky, V. P. Polyakova, N. B. Gorina and N. R. Roshan, “Physical Metallurgy of Platinum Metals”, Metallurgiya Publishers, Moscow, Russia, 1975 (in Russian); English translation, Mir Publishers, Moscow, Russia, 1978
- P. Battaini, ‘The Metallography of Platinum and Platinum Alloys’, in “The Santa Fe Symposium on Jewelry Manufacturing Technology 2010”, ed.E. Bell, Proceedings of the 24th Symposium in Albuquerque, New Mexico, USA, 16th–19th May, 2010, Met-Chem Research Inc, Albuquerque, New Mexico, USA, 2010, pp. 27–49
- M. Grimwade, “Introduction to Precious Metals: Metallurgy for Jewelers and Silversmiths”, Brynmorgen Press, Brunswick, Maine, USA, 2009
- J. Maerz, ‘Platinum Alloy Applications for Jewelry’, in “The Santa Fe Symposium on Jewelry Manufacturing Technology 1999”, ed.D. Schneller, Proceedings of the 13th Symposium in Albuquerque, New Mexico, USA, 16th–19th May, 1999, Met-Chem Research Inc, Albuquerque, New Mexico, USA, 1999, pp. 55–72
- J. Huckle, ‘The Development of Platinum Alloys to Overcome Production Problems’, in “The Santa Fe Symposium on Jewelry Manufacturing Technology 1996”, ed.D. Schneller, Proceedings of the 10th Symposium in Albuquerque, New Mexico, USA, 19th–22nd May, 1996, Met-Chem Research Inc, Albuquerque, New Mexico, USA, 1996, pp. 301–326
- D. P. Agarwal and G. Raykhtsaum, ‘Manufacturing of Lightweight Platinum Jewelry and Findings’, in “The Santa Fe Symposium on Jewelry Manufacturing Technology 1996”, ed.D. Schneller, Proceedings of the 10th Symposium in Albuquerque, New Mexico, USA, 19th–22nd May, 1996, Met-Chem Research Inc, Albuquerque, New Mexico, USA, 1996, pp. 373–382
- J. Maerz, ‘Platinum Alloys: Features and Benefits’, in “The Santa Fe Symposium on Jewelry Manufacturing Technology 2005”, ed.E. Bell, Proceedings of the 19th Symposium in Albuquerque, New Mexico, USA, 22nd–25th May, 2005, Met-Chem Research Inc, Albuquerque, New Mexico, USA, 2005, pp. 303–312
- R. Lanam, F. Pozarnik and C. Volpe, ‘Platinum Alloy Characteristics: A Comparison of Existing Platinum Casting Alloys with Pt-Cu-Co’, Technical Articles: Alloys, Platinum Guild International, USA, 1997: http://www.platinumguild.com/output/page2414.asp (Accessed on 31 December 2010)
- G. Normandeau and D. Ueno, ‘Platinum Alloy Design for the Investment Casting Process’, Technical Articles: Alloys, Platinum Guild International, USA, 2002: http://www.platinumguild.com/output/page2414.asp (Accessed on 31 December 2010)
- R. F. Vines and E. M. Wise, “The Platinum Metals and Their Alloys”, The International Nickel Company, Inc, New York, USA, 1941
- “Handbook of Precious Metals”, ed.E. M. Savitsky, Metallurgiya Publishers, Moscow, Russia, 1984 (in Russian); English translation, Hemisphere Publishing Corp, New York, USA, 1989
- K. Vaithinathan and R. Lanam, ‘Features and Benefits of Different Platinum Alloys’, Technical Articles: Alloys, Platinum Guild International, USA, 2005: http://www.platinumguild.com/output/page2414.asp (Accessed on 31 December 2010) LINK http://www.platinumguild.com/output/page2414.asp
- P. Battaini, Platinum Metals Rev., 2011, 55, (1), 71 LINK http://www.platinummetalsreview.coms/dynamic/article/view/55-1-71-72
- D. Miller, T. Keraan, P. Park-Ross, V. Husemeyer and C. Lang, Platinum Metals Rev., 2005, 49, (3), 110 LINK http://www.platinummetalsreview.com/article/49/3/110-117
- J. C. McCloskey, ‘Microsegregation in Pt-Co and Pt-Ru Jewelry Alloys’, in “The Santa Fe Symposium on Jewelry Manufacturing Technology 2006”, ed.E. Bell, Proceedings of the 20th Symposium in Nashville, Tennessee, USA, 10th–13th September, 2006, Met-Chem Research Inc, Albuquerque, New Mexico, USA, 2006, pp. 363–376
- “Smithells Metals Reference Book”, 7th Edn., eds.E. A. Brandes and G. B. Brook, Butterworth-Heinemann, Ltd, Oxford, UK, 1992
- R. W. Cahn, ‘Recovery and Recrystallization’, in “Physical Metallurgy”, eds.R. W. Cahn and P. Haasen, Elsevier Science BV, Amsterdam, The Netherlands, 1996
- P. R. Munroe, Mater. Charact., 2009, 60, (1), 2 LINK http://dx.doi.org/10.1016/j.matchar.2008.11.014
- E. Bemporad, ‘Focused Ion Beam and Nano-Mechanical Tests for High Resolution Surface Characterization: Not So Far Away From Jewelry Manufacturing’, in “The Santa Fe Symposium on Jewelry Manufacturing Technology 2010”, ed.E. Bell, Proceedings of the 24th Symposium in Albuquerque, New Mexico, USA, 16th–19th May, 2010, Met-Chem Research Inc, Albuquerque, New Mexico, USA, 2010, pp. 50–78
- D. J. Shuman, A. L. M. Costa and M. S. Andrade, Mater. Charact., 2007, 58, (4), 380 LINK http://dx.doi.org/10.1016/j.matchar.2006.06.005
Paolo Battaini holds a degree in nuclear engineering and is a consultant in failure analysis for a range of industrial fields. He is responsible for research and development at 8853 SpA in Milan, Italy, a factory producing dental alloys and semi-finished products in gold, platinum and palladium alloys, and is currently a professor of precious metal working technologies at the University of Milano-Bicocca, Italy. Professor Battaini is also a recipient of the Santa Fe Symposium® Ambassador Award and regularly presents at the Santa Fe Symposium® on Jewelry Manufacturing Technology.